Name	Resin reactivity	Type	Non-volatile content, % (BNS EN ISO 3251)	Viscosity at Brookfield, mPa.s (ISO 2555)	Gel time - min,T°C	Gel time - Catalyst system	Acid number, mgKOH/g (BNS EN ISO 3682)	Gardner colour (BNS EN ISO 4630)	Hazen colour (BNS ISO 2211)	Modiffication	Tensile strenght, Mpa (BNS EN ISO 527-1,2)	Flexural strenght, Mpa (BNS EN ISO 178)	HDT,°C (BNS EN ISO 75-1,2)	Barcol Hardnes (ASTM D 2583)	Applications	TDS	Safety
Vinalkdy 450 P	HR	O	65-67	950-1250 at 23°C	8-16 at 20°C	1% Co-1% ,4% MEKP-50	max.27	max.2	*	A	*	min. 128	min. 78	min. 45	FG Fibreglasss articles		N/A
Vinalkyd 550 PE-R	HR	O	64-66	550-850 at 25°C	6-9 at 25°C	1,2% Co-2%, 2% MEKP-50	max.30	max.2	*	A/LV	min.70	min.140	min.67	min.50	FG Fibreglasss articles		N/A
Vinalkyd 550 PE-R/61	HR	O	59-63	400-550 at 23°C	10-30 at 20°C	1 % Co-1% , 2 % MEKP-50	max.30	max.2	*	A	min.70	min.120	min.64	min.45	FG Fibreglasss articles		N/A
Vinalkyd 550 R 62 LSE	HR	O	61-63	500-600 at 23°C	10-20 at 23°C	1 % Co-1% , 2 % MEKP-50	max.30	*	*	A	min.68	min.130	min.68	min.45	FG Fibreglasss articles		N/A
Vinalkyd 901 PE-A	MR	O	68-70	900-1250 at 25°C	3'30''-5'30'' at 35°C	2% MEKP-50	max.32	*	*	*	min.60	min.120	min.60	min.50	FG Fibreglasss articles		N/A
Vinalkyd 901 PE-A(LV)	MR	O	68-72	700-950 at 25°C	8-10 at 35°C	2% MEKP-50	max.32	*	*	*	min.60	min.120	min.60	min.50	FG Fibreglasss articles		N/A
Vinalkyd 620 PE-A	MR	O	58,5-61,5	180-320 at 25°C	10-20 at 25°C	1% MEKP-50	max.30	*	*	*	*	*	*	*	SF Sanitary faience		N/A
Vinalkyd 801 PE-A	MR	O	65-67	450-650 at 25°C	7-11 at 25°C	1,5 % MEKP-50	max.32	*	*	*	*	*	*	*	SF Sanitary faience		N/A
Vinalkyd 520 PD	MR	O	min. 55	175-350 at 25°C	10-20 at 25°C	1%Co-1%, 1,0% MEKP-60	max.30	*	max.300	*	min.70	min.120	*	min.40	ML Machine Laminating		N/A
Vinalkyd 25 PE	MR	ISO	64-66	600-900 at 23°C	6-12 at 25°C	1% Co-1%, 1,5% MEKP-50	max.30	max.2,5	*	A	min.77	min.130	min.90	*	FG Fibreglasss articles		N/A
Vinalkyd 350 NPP	HR	ISO/NPG	59-61	450-650 at 25°C	6-9 at 25°C	1% Co-1%, 1,5% MEKP-50	max.14	max.1	*	A	min.65	*	min.85	min.45	FG Fibreglasss articles		N/A
Vinalkyd 520PD-59	MR	Ortho	59+/-2	300-450	4-6	3% Co-6%, 2% MEKP-50	max 23	max 2	*	*	min 70	min 120	min 95	min 40	FG Fibreglasss articles		N/A
Vinalkyd 520PD-60	MR	Ortho	61+/-1,5	300-500	10-20	1% Co-1%, 1,1% MEKP-50	max 23	*	max 300	*	min 70	min 120	*	min 40	FGSF Fibreglasss articles Sanitary faience		N/A
Vinalkyd 451 P (SMC/BMC)	HR	O	64+/-2%	1400-1800	10-16 min	1 % Perkadox CH-50 X	15-20		max 150		min 60 MPa	min 120 MPa	min 110С	min 50	ML Machine Laminating		N/A
Vinalkyd 350 NPP/66	MR		66+/-2%	900 - 1100	8-14	1,0 g Butanox M-50	max 14				min 65	min 3300	min 65C	min 40	ML Machine Laminating		N/A

A - accelerated, LV - low Viscosity, LSE - low sturene emission

Name	Type	Non-volatile content % (BNS EN ISO 3251)	Viscosity at Brookfield, mPa.s (ISO 2555)	Gel time - min,T°C	Gel time - Catalyst system	Tixotropic index - ASTM D 2196-05 (B)	Modiffication	Tensile strenght, Mpa (BNS EN ISO 527-1,2)	Flexural strenght, Mpa (BNS EN ISO 178)	HDT, °C (BNS EN ISO 75-1,2)	Barcol Hardnes (ASTM D 2583)	Applications	TDS	Safety
Vinalkyd 550 PE-TALV-1	O	56-58	1100-1300 at 23°C	15-25 at 23°C	2% MEKP-50	min. 2,4	B/LE	min.60	min.120	min.79	min.50	H Hand lay-up		N/A
Vinalkyd 550 PE-TALV-2	O	55-57	800-1000 at 23°C	5-10 at 23°C	2% MEKP-50	min. 2,4	B/LE	*	*	*	*	HS Hand lay-up Spray up		N/A
Vinalkyd 550 PE-TA-LE-B	O	56-58	1100-1300 at 23°C	30-40 at 20°C	1,5% MEKP-50	min.2,8	B/FC	min.69	min.117	min.63	min.47	H Hand lay-up		N/A
Vinalkyd 550 PE-TA-LSE/B	O	56-58	1100-1300 at 23°C	15-25 at 23°C	2% MEKP-50	min.2,8	*	*	*	*	*	H Hand lay-up		N/A
Vinalkyd 550 PE-TALE-LV	O	56-60	800-1000 at 23°C	11-21 at 20°C	2% MEKP-50	min. 2,4	B/FC	min.65	min.115	min.63	min.45	HS Hand lay-up Spray up		N/A
Vinalkyd 550 PE-TALV-LE-B	O	55-57	800-1000 at 23°C	15-25 at 23°C	2% MEKP-50	min. 2,4	*	min.65	min.125	*	min.50	HS Hand lay-up Spray up		N/A
Vinalkyd 620 PE-TALV-1	O	59-61	300-500 at 25°C	7-14 at 25°C	1% MEKP-50	min.1,0	B	*	*	*	*	HS Hand lay-up Spray up		N/A
Vinalkyd 620 PE-TALV-2W	O	51-53	140-240 at 25°C	7-12 at 25°C	1% MEKP-50	min.1,4	B	*	*	*	*	HS Hand lay-up Spray up		N/A
Vinalkyd 25 PE-ATA	ISO	54-56	750-900 at 23°C	10-20 at 23°C	2% MEKP-50	min. 2,4	B	*	*	*	*	HS Hand lay-up Spray up		N/A
Vinalkyd 901 R-TA-B		58 +/- 1,5 %	500-600		23-33 min	min 2,8						HRFGSFML Unsaturated? Fibreglasss articles Sanitary faience Machine Laminating		N/A
Vinalkyd 520PD-TALE-B	Ortho	65	800-1100	15-25	2% MEKP-50%	min 2,5	*	*	*	*	*	FG Fibreglasss articles		N/A
Vinalkyd 520PD-TA-BLE	Ortho	57+/-1,5	800-1100	20-27	1,5% MEKP-50	min 1,8	A	min 70	min 120	min 95	min 40	FGSF Fibreglasss articles Sanitary faience		N/A
Vinallkyd 550 PE-TA-LV	Ortho	58+/-2	600-800	20-30	1,5% MEKP-50	min 3	A	min 65	min 115	min 63	min 40	FGSFML Fibreglasss articles Sanitary faience Machine Laminating		N/A
Vinalkyd 550PE-T	Ortho	57+/-1	1100-1300	30-40	0,6 % Co-1%, 1,5 % MEKP-50	min 2,4	*	min 69	min 117	63	min 48	FGSFML Fibreglasss articles Sanitary faience Machine Laminating		N/A

A - accelerated, Т - toluene, LV - low viscosity, LE/LSE - low sturene emission, FC - fast Curing, W - white colored, B - blue colored (peroxide indicator)

Name	Type	Non-volatile content % (BNS EN ISO 3251)	Viscosity at Brookfield, mPa.s (ISO 2555)	Gel time - min,T°C	Gel time - Catalyst system	Tixotropic index - ASTM D 2196-05 (B)	Applications	TDS	Safety
Isophtalic brush Gelcoat G-2-A	ISO	63-67	33000-43000 6000-9000 at 25°C	10-15 at 20°C	2 % MEKP-50	min. 5.0	H Hand lay-up		N/A
Isophtalic spray Gelcoat G-2-A-S	ISO	59-63	3500-7000 at 25°C	10-18 at 25°C	2 % MEKP-50	min. 5.0	S Spray up		N/A
ISO Topcoat White	ISO	67+/-2%	5000-8000	10-20	2% MEKP-50	min. 4,5	HS Hand lay-up Spray up		N/A
Orthophtalic brush Gelcoat G-1-A	ORTHO	65+/-2%	33000-43000 sp. 2, 2 rpm	10-15		min. 5,0	H Hand lay-up		N/A
Isophtalic spray white Gelcoat G-2-W	ISO	65+/-2%	3000-4000	12-18	2% MEKP	min 4,5	S Spray up		N/A
ISO/NPG spray Gelcoat G-3-A	ISO/NPG	55+/-2%	6000-8000	6-13		min.5	S Spray up		N/A

A - accelerated, ISO - isophthalic based resin, NPG - neopentil glycol based resin, W - white colored, S - soya oil or sunflower oils